The Effect of Organic Contaminants on the Microstructure-Based Mechanical and Durability Parameters of Concrete Containing Polluted Aggregate Materials

Document Type : Research Paper

Authors

1 Associate Professor, University of Hormozgan, Faculty of Engineering, Bandar Abbas, Iran

2 Master Student, University of Hormozgan, Faculty of Engineering, Bandar Abbas, Iran.

10.22124/jcr.2023.24670.1622

Abstract

Industrial activities, particularly in petrochemical and refinery sectors, have introduced a wide range of organic pollutants into the environment, leading to the pollution of aggregate materials with crude oil or petroleum products. This study investigates the influence of aggregate materials contaminated with crude oil and diesel on the cement hydration process and concrete properties. Around 90 concrete samples with polluted aggregates were evaluated over a 6-month period. Compressive strength tests and water absorption percentage tests were conducted at different ages. Microstructural analysis through SEM, structural analysis via EDX, and XRD analysis for hydration product characterization were performed. Results showed a significant reduction in compressive strength (47% and 31%) for samples contaminated with crude oil and diesel, respectively, compared to the control. Water absorption and permeability increased in polluted samples. SEM, and XRD, results indicated increased ettringite production, decreased nanostructure C-S-H, reduced strength and durability, and increased water absorption and permeability in the concrete. This study highlights the detrimental effects of organic contaminants on concrete properties, emphasizing the need for pollution management in aggregate materials for sustainable construction practices.

Keywords

Main Subjects

References

[1].Wang, S., H. Jia, J. Lu, and D. Yang, Crude oil transportation route choices: A connectivity reliability-based approach. Reliability Engineering & System Safety, 2023. 235: p. 109254.
[2]Rezaei, A., M. Rowshanzamir, S.M. Hejazi, and M. Banitalebi-Dehkordi, Application of superabsorbent geotextiles to decontaminate and improve crude oil-contaminated soil. Transportation Geotechnics, 2023. 38: p. 100910.
[3].Radhakrishnan, A., P. Balaganesh, M. Vasudevan, N. Natarajan, A. Chauhan, J. Arora, A. Ranjan, V.D. Rajput, S. Sushkova, and T. Minkina, Bioremediation of Hydrocarbon Pollutants: Recent Promising Sustainable Approaches, Scope, and Challenges. Sustainability, 2023. 15(7): p. 5847.
[4].Shoushtari, M., A. Lashkari, and A. Martinez, Effect of gas-oil contamination on the mechanical behavior of sand-woven geotextile interface: Experimental investigation and constitutive modeling. Geotextiles and Geomembranes, 2023.
[5].Lange, I., P. Kotiukov, and Y. Lebedeva, Analyzing Physical-Mechanical and Hydrophysical Properties of Sandy Soils Exposed to Long-Term Hydrocarbon Contamination. Sustainability, 2023. 15(4): p. 3599.
[6].Abousnina, R. and R.L. Allister, Oil contaminated sand: sources, properties, remediation, and engineering applications. Sand in construction, 2022.
[7].Karabash, Z., M.A. Al-Obaydi, M.A. Awad, and M.N. Al-Khashab, Geotechnical Properties of Clay Soil Contaminated with Different Types of Oil. Geotechnical and Geological Engineering, 2023.
[8].Haghsheno, H. and M. Arabani, Geotechnical properties of oil-polluted soil: a review. Environmental Science and Pollution Research, 2022. 29(22): p. 32670-32701.
[9].Osuji, S. and E. Nwankwo, Effect of crude oil contamination on the compressive strength of concrete. Nigerian Journal of Technology, 2015. 34(2): p. 259-265.
[10].Diab, H., Compressive strength performance of low-and high-strength concrete soaked in mineral oil. Construction and Building Materials, 2012. 33: p. 25-31.
[11].Svintsov, A.P. and S.L. Shambina, Influence of viscosity of vegetable and mineral oil on deformation properties of concrete and cement-sand mortar. Construction and Building Materials, 2018. 190: p. 964-974.
[12].Al-Khateeb, R., H.T. Naeem, and B. Abdul, Influence of Gas Oil on Compressive Strength of Concrete. International Journal of General Engineering and Technology (IJGET). 3(1): p. 51-56.
[13].Kadhum, M.M., N.A. Alwash, W.K. Tuama, and M.S. Abdulraheem, Experimental and numerical study of influence of crude oil products on the behavior of reactive powder and normal strength concrete slabs. Journal of King Saud University-Engineering Sciences, 2020. 32(5): p. 293-302.
[14].Ejeh, S. and O. Uche, Effect of crude oil spill on compressive strength of concrete materials. Journal of applied sciences Research, 2009. 5(10): p. 1756-1761.
[15].Ajagbe, W.O., O.S. Omokehinde, G.A. Alade, and O.A. Agbede, Effect of crude oil impacted sand on compressive strength of concrete. Construction and Building Materials, 2012. 26(1): p. 9-12.
[16].Abousnina, R.M., A. Manalo, and W. Lokuge, Physical and mechanical properties of cement mortar containing fine sand contaminated with light crude oil. Procedia Engineering, 2016. 145: p. 250-258.
[17].Abednego, G., O. Ishmael, O. Achemie, A. Paul, and S. Samuel, Effects of crude oil contaminant on the engineering properties of concrete. Am. J. Civil Engr, 2015. 3(5): p. 178-182.
[18].Abousnina, R., A. Manalo, W. Lokuge, and K.S. Al-Jabri, Properties and structural behavior of concrete containing fine sand contaminated with light crude oil. Construction and Building Materials, 2018. 189: p. 1214-1231.
[19].Javadli, R. and A. De Klerk, Desulfurization of heavy oil. Applied petrochemical research, 2012. 1: p. 3-19.
[20].ASTM, C33, Standard Test Method for Sieve Analysis of Fine and Coarse Aggregates. ASTM International, West Conshohocken, PA (2006).
[21].ASTM, C39, Standard test method for compressive strength of cylindrical concrete specimens. ASTM International, West Conshohocken, PA (2010).
[22].ASTM, C128-07a, Standard Test Method for Density, Relative Density (Specific Gravity), and Absorption of Fine Aggregate. ASTM International: West Conshohocken, PA (2007).
[23].ASTM, C127 ، Standard Test Method for Density, Relative Density (Specific Gravity), and Absorption of coarse aggregatesASTM International, West Conshohocken, PA (2007).
[24].ASTM, C204-07, Standard Test Methods for Fineness of Hydraulic Cement by Air-Permeability Apparatus. ASTM International, West Conshohocken, PA (2009).
[25].1048, D., Concrete harden-Determination of the depth of penetration of water under pressure German National Standard, 1991.
[26].Singh, A., Strength and permeability characteristics of steel fibre reinforced concrete. International Journal of Civil and Environmental Engineering, 2013. 7(10): p. 733-738.
[27].INSO, 1608-122., 1st.Editio. 2018.
[28].Zeyad, A.M., M.A.M. Johari, Y.R. Alharbi, A.A. Abadel, Y.M. Amran, B.A. Tayeh, and A. Abutaleb, Influence of steam curing regimes on the properties of ultrafine POFA-based high-strength green concrete. Journal of Building Engineering, 2021. 38: p. 102204.
[29].Asakereh, A. and M. Amiri, Microstructural Study of Soil Stabilization of the Southern Marl Using Lime and Nano-SiO2. Modares Civil Engineering journal, 2019. 19(3): p. 111-122.
[30].Ouhadi, V., R. Yong, M. Amiri, and M. Ouhadi, Pozzolanic consolidation of stabilized soft clays. Applied Clay Science, 2014. 95: p. 111-118.
[31].Zhang, M., L. Du, Z. Li, and R. Xu, Durability of marine concrete doped with nanoparticles under joint action of Cl-erosion and carbonation. Case Studies in Construction Materials, 2023. 18: p. e01982.
[32].Lee, C., H. Lee, and K. Lee, Strength and microstructural characteristics of chemically activated fly ash–cement systems. Cement and Concrete Research, 2003. 33(3): p. 425-431.
[33].Ghorab, H., M. Mabrouk, D. Herfort, and Y. Osman, Infrared investigation on systems related to the thaumasite formation at room temperature and 7 C. Cem. Wapno Beton, 2014. 4: p. 252-261.
[34].Mehta, P.K. and P.J. Monteiro, Concrete: microstructure, properties, and materials. 2014: McGraw-Hill Education.
[35].Richardson, I. and G. Groves, Microstructure and microanalysis of hardened ordinary Portland cement pastes. Journal of Materials science, 1993. 28: p. 265-277.
[36].Ramezanianpour, A.A., E. Ghiasvand, and M.E. Kamel, Durability of Concretes and Mortars Containing Limestone Powder Exposed to High Sulfate Environments. Amirkabir Journal of Civil Engineering, 2012. 43(2): p. 19-25.
[37].Anwar, A., B.S. Mohammed, M. Liew, M.A. Wahab, and N.A.W.A. Zawawi, Below-grade sulfur storage pits in oil refineries: a review. Journal of Failure Analysis and Prevention, 2019. 19: p. 1745-1760.
[38].Alhelal, Z.S., Sulfur storage pits in petrochemical plants: deterioration mechanism, materials selection, and repair. Practice Periodical on Structural Design and Construction, 2014. 19(2): p. 04014005.
[39].Abousnina, R., A. Manalo, W. Ferdous, W. Lokuge, B. Benabed, and K.S. Al-Jabri, Characteristics, strength development and microstructure of cement mortar containing oil-contaminated sand. Construction and Building Materials, 2020. 252: p. 119155.
[40].Amiri, M. and Tanideh. P, Microstructural Assessment of the Effect of Sulfate Environments on the Mechanical Properties of Concrete. 2020.
[41].Ayininuola, G.M., Influence of diesel oil and bitumen on compressive strength of concrete. Journal of civil engineering, 2009. 37(1): p. 65-71.
[42].CEB-FIP, Diagnosis and assessment of concrete structures–state of art report. CEB Bull, 1989. 192: p. 83-85.